Título: Comparison between calcium carbonate and β-tricalcium phosphate as additives of 3D printed scaffolds with polylactic acid matrix
Autores/as: Donate González, Ricardo 
Monzón, Mario 
Ortega, Zaida 
Wang, Ling
Ribeiro, Viviana
Pestana Guillén, Jesús David 
Oliveira, Joaquim M.
Reis, Rui L.
Clasificación UNESCO: 3313 Tecnología e ingeniería mecánicas
32 Ciencias médicas
Palabras clave: Additive manufacturing
Bone regeneration
Calcium carbonate
Metabolic activity
Tissue engineering, et al.
Fecha de publicación: 2020
Proyectos: Biomaterials And Additive Manufacturing: Osteochondral Scaffold Innovation Applied To Osteoarthritis 
Mejora de la Biofuncionalidad de Scaffolds Polimericos Obtenidos Por Fabricacion Aditiva 
Publicación seriada: Journal of tissue engineering and regenerative medicine 
Resumen: In this study, polylactic acid (PLA)‐based composite scaffolds with calcium carbonate (CaCO3) and beta‐tricalcium phosphate (β‐TCP) were obtained by 3D printing. These structures were evaluated as potential 3D structures for bone tissue regeneration. Morphological, mechanical, and biological tests were carried out in order to compare the effect of each additive (added in a concentration of 5% w/w) and the combination of both (2.5% w/w of each one), on the PLA matrix. The scaffolds manufactured had a mean pore size between 400–425 μm and a porosity value in the range of 50–60%. According to the results, both additives promoted an increase of the porosity, hydrophilicity, and surface roughness of the scaffolds, leading to a significant improvement of the metabolic activity of human osteoblastic osteosarcoma cells. The best results in terms of cell attachment after 7 days were obtained for the samples containing CaCO3 and β‐TCP particles due to the synergistic effect of both additives, which results in an increase in osteoconductivity and in a microporosity that favours cell adhesion. These scaffolds (PLA:CaCO3:β‐TCP 95:2.5:2.5) have suitable properties to be further evaluated for bone tissue engineering applications.
URI: http://hdl.handle.net/10553/69434
ISSN: 1932-7005
DOI: 10.1002/term.2990
Fuente: Journal of tissue engineering and regenerative medicine [ISSN 1932-7005], v. 14 (2), p. 272-383
Colección:Artículos
miniatura
Pre-print
Adobe PDF (2,05 MB)
Vista completa

Google ScholarTM

Verifica

Altmetric


Comparte



Exporta metadatos



Los elementos en ULPGC accedaCRIS están protegidos por derechos de autor con todos los derechos reservados, a menos que se indique lo contrario.