Identificador persistente para citar o vincular este elemento: http://hdl.handle.net/10553/75403
Título: Study on the anode-protection, applied to industrial interest metals and alloys
Autores/as: Santana, GG
Lopez, AS
Mirza Rosca, Julia Claudia 
Vasilescu, C
Clasificación UNESCO: 3328 Procesos tecnológicos
Palabras clave: Steel
Aisi 304 Stainless Steel
Aluminum
Anodic Protection
Carbon Steel
Fecha de publicación: 2001
Publicación seriada: Revista de Chimie 
Resumen: Using potentiostatic polarization technique were studied the anodic protection of carbon steel in Kraft solution(paper industry), of AISI304 stainless steel in 10% HCl and 10N H2SO4+ 10(-5) M NaCl and of aluminium in 0.2% NaOH. Applying anodic protection the carbon steel corrosion rate was diminished by 40 times in Kraft solution: for AlSI304 stainless steel it resulted a reduction of corrosion rate by 20 times in 10% HCl and by 60 times in 10N H2SO4 + 10(-5) M NaCl. The aluminium corrosion decreased by 6 times in anodic protection conditions applied in 0.2% NaOH.
URI: http://hdl.handle.net/10553/75403
ISSN: 0034-7752
Fuente: Revista De Chimie[ISSN 0034-7752],v. 52 (10), p. 572-575, (Octubre 2001)
Colección:Artículos
Vista completa

Citas de WEB OF SCIENCETM
Citations

1
actualizado el 25-feb-2024

Visitas

81
actualizado el 03-feb-2024

Google ScholarTM

Verifica


Comparte



Exporta metadatos



Los elementos en ULPGC accedaCRIS están protegidos por derechos de autor con todos los derechos reservados, a menos que se indique lo contrario.