Título: Electrochemical characterization of some cobalt base alloys in Ringer solution
Autores/as: Garcia-Falcon, C. M.
Gil-Lopez, T.
Verdu-Vazquez, A.
Mirza Rosca, Julia Claudia 
Clasificación UNESCO: 330307 Tecnología de la corrosión
321313 Ortodoncia-estomatología
Palabras clave: Corrosion
Co–Cr
Dental Materials
Metal Alloys
Ringer Solution
Fecha de publicación: 2021
Publicación seriada: Materials Chemistry and Physics 
Resumen: Biomaterials should be thoroughly studied in order to make sure they do not cause any harm to the human body. Considering that biocompatibility is very strict, the material must be non-toxic, and not cause any allergies or inflammation in the body. Of the different categories of metallic biomaterials, the cobalt-based alloys are among the preferred options. Applications can be found in orthopedic implants, and both cardiac and dental fields. Co–Cr alloys have been used in dentistry for porcelain-fused-to-metal (PFM) crowns due to their biocompatibility, wear resistance, long service duration, good mechanical properties, and last but not least, superior resistance to corrosion. The present investigation evaluated and compared two Co–Cr based dental alloys, studying their microstructural characterization and corrosion behavior in Ringer solution, using various techniques. Findings in this investigation revealed a high passivation tendency for the two alloys studied, with the formation of mixed protective layers Cr2O3·CoO with high stability on their surfaces, which substantially improves their biocompatibility in Ringer solution. The kinetic parameters of the corrosion process in the experiment indicated a two-time constants process with an anodic control, attributable to the formation of passive films on their surfaces. According to the results obtained in this investigation, the polarization resistance of the two Co–Cr alloys examined in Ringer solution reached the values of biomaterials with a high resistance to corrosion, and the passive films formed on their surface had a more than appropriate resistance to corrosion.
URI: http://hdl.handle.net/10553/77540
ISSN: 0254-0584
DOI: 10.1016/j.matchemphys.2020.124164
Fuente: Materials Chemistry and Physics[ISSN 0254-0584], v. 260, 124164, (Febrero 2021)
Colección:Artículos
Vista completa

Citas SCOPUSTM   

14
actualizado el 24-mar-2024

Visitas

108
actualizado el 11-feb-2023

Google ScholarTM

Verifica

Altmetric


Comparte



Exporta metadatos



Los elementos en ULPGC accedaCRIS están protegidos por derechos de autor con todos los derechos reservados, a menos que se indique lo contrario.